High Quality And Large Size LiNbO3 Widely Used As A Birefringent Crystal For Fiber Optic Communication
Product overview:
LiNbO3 Crystal is widely used as frequency doublers for wavelength > 1 mm and OPOs pumped at 1064 nm as well as QPM devices.
LiNbO3 Crystal is widely used as frequency doublers for wavelength>1 µm and optical parametric oscillators(OPOs) pumped at 1064nm and quasi-phase-matched(QPM)devices.Additionally due to its large Electro-Optic (E-O)and Acousto-Optic(A-O)coefficients.
LiNbO3 is the most commonly used material for Pockels Cells,Q-Switches and phase nodulators,wavwguide substrate,and surface acoustic wave (SAW)
wafers,etc.we can provide high quality and large size LiNbO3 crystals for all of these applications.
Structural and Physical Properties of LiNbO3
| Crystal Structure: |
Trigonal, Space group Rjc, Point group 3m |
| Cell Parameters: |
a=5.148Å,c=13.863Å |
| Melting Point: |
1253℃ |
| Curie Temperature: |
1140℃ |
| Mohs Hardness: |
5 |
| Density: |
4.64g/cm3 |
| Elastic Stiffness Coefficients: |
CE11=2.33(x 1011N/m2) |
| CEJJ= 2.77(x 1011N/m2) |
Optocal and Electro-optical kaibukai Properties of LiNbO3
| Transparency Range: |
420-5200nm |
| Optical Homogeneity: |
~5X10-5/cm |
| Refractive indices at 1064nm: |
ne=2.146, na=2.220@1300nm |
| ne=2.156, na=2.232@1064nm |
| ne=2.203, na=2.286@632.8nm |
| NLO Coefficients: |
dJJ=86XdJ6(KDP) |
| dJ1=11.6XdJ6(KDP) |
| d22=5.6XdJ6(KDP) |
| Effective NLO Coefficients: |
deπ(Ⅰ)=dJ1sinθ-d22cossin3φ |
| deπ(Ⅱ)=d22cos2θcos3φ |
| Haif-Wave Voltage,DC |
3.03KV |
| Electrical field//z, light z: |
4.02KV |
| Electrical field//x or y, light// z: |
|
| Damage Threshold: |
100MW/cm2(10ns,1064nm) |
Thermal and Electrical Properties of LiNbO3
| Melting Point: |
1250℃ |
| Cruie Temperature: |
1140℃ |
| Thermal Conductivity: |
38W/m@25℃ |
| Thermal Expansion Coefficients(at 25℃) |
//a,2.0x10-6/K |
| //c,2.2 x10-6/K |
| Resistivity: |
2x10-6Ω cm@200℃ |
| Dielectric Constants: |
εs11/εD=43 εT11/εD=78 |
| εs11/εD=28 εsJJ /εD =43 |
Specifications
Transmitting wavefront distortion:less than λ/4 @633nm
Dimension tolerance:(W+-0.1mm) x(H+-0.1mm) x (L+-0.2mm)
Clear aperture:>90% central area
Flatness:λ/8 @633nm
Angle tolerance:<+-0.5°
AR coating:dual wave band AR coating at 1064/532 nm on both surface,with R<0.2% at 1064nm
and R<0.5% at 532nm per surface.Other coatings are avaliable upon request.